| Au 750/3150 Pd | ||||
| Colour | white | Code | 3150 | |
| General description | 18 ct white gold nickel-free alloy containing Pd. It can easily be rolled, drawn, polished and machined. Not recommended for casting and stamping. It does not require Rhodium plating. |
|---|
| Physical properties | Specific gravity [g/cm3] | 15.7 | Melting range [°C] | 1125-1195 |
|---|
| Mechanical properties | Annealed | 20% cold worked | 75% cold worked | ||
|---|---|---|---|---|---|
| Vickers hardness | [HV1] | 160 | 225 | 260 | |
| Yield hardness | Rm | [Mpa] | 600 | 790 | 960 |
| Elastic limit | Rp0.2 | [MPa] | 360 | 670 | 890 |
| Plastic elongation | A | [%] | 35 | 2 | 1 |
| Processing guidelines | |
|---|---|
| ANNEALING | 800 °C for 20 to 30 minutes then quenched in water. In order to avoid oxidation, work under reducing atmosphere. |
| COLD WORKING | The amount of coldwork completed before annealing should be between 30% and 75% reduction in area. |
| SOLDERING | By torch or furnace. The nickel-free solders N° 3532 (840-910 °C), 3534 (750-810 °C) and 3535 (650-780 °C) are strongly recommended. For alternatives please see list of solders. |
| PICKLING | with DESOXYD (following operating instructions) or with hot 10% sulphuric acid added to hot 10 g/l ammonium persulphate. The slight change of colour which could appear can be removed by polishing. |
| - | - |
| - | - |